Interpenetrated Networks between Graphitic Carbon Infilling and Ultrafine TiO2 Nanocrystals with Patterned Macroporous Structure for High-Performance Lithium Ion Batteries
发表时间：2019-03-12
点击次数：
- 论文类型：
- 期刊论文
- 第一作者：
- Zheng, Wenji
- 通讯作者：
- Li, XC (reprint author), Dalian Univ Technol, Dept Chem Engn, State Key Lab Fine Chem, Linggong Rd 2, Dalian 116024, Peoples R China.
- 合写作者：
- Yan, Zhijun,Dai, Yan,Du, Naixu,Jiang, Xiaobin,Dai, Hailing,Li, Xiangcun,He, Gaohong
- 发表时间：
- 2017-06-21
- 发表刊物：
- ACS APPLIED MATERIALS & INTERFACES
- 收录刊物：
- SCIE、EI、PubMed、Scopus
- 文献类型：
- J
- 卷号：
- 9
- 期号：
- 24
- 页面范围：
- 20491-20500
- ISSN号：
- 1944-8244
- 关键字：
- TiO2; macropore; mesopore; Li ion battery; carbon
- 摘要：
- Interpenetrated networks between graphitic carbon infilling and ultrafine TiO2 nanocrystals with patterned macropores (100-200 nm) were successfully synthesized. Polypyrrole layer was conformably coated on the primary TiO2 nanoparticles (similar to 8 nm) by a photosensitive reaction and was then transformed into carbon infilling in the interparticle mesopores of the TiO2 nanoparticles. Compared to the carbon/graphene supported TiO2 nanoparticles or carbon coated TiO2 nanostructures, the carbon infilling would provide a conductive medium and buffer layer for volume expansion of the encapsulated TiO2 nanoparticles, thus enhancing conductivity and cycle stability of the C-TiO2 anode materials for lithium ion batteries (LIBs). In addition, the macropores with diameters of 100-200-nm in the C-TiO2 anode and the mesopores in carbon infilling could improve electrolyte transportation in the electrodes and shorten the lithium ion diffusion length. The C-TiO2 electrode can provide a large capacity of 192.8 mA h g(-1) after 100 cycles at 200 mA g(-1), which is higher than those of the pure macroporous TiO2 electrode (144.8 mA h g(-1)), C-TiO2 composite electrode without macroporous structure (128 mA h g(-1)) and most of the TiO2 based electrodes in the literature. Importantly, the C-TiO2 electrode exhibits a high rate performance and still delivers a high capacity of similar to 440 mA h g(-1) after 1000 cycles at 1000 mA g(-1) (similar to 5.88 C), suggesting good lithium storage properties of the macroporous C-TiO2 composites with high capacity, cycle stability, and rate capability. This work would be instructive for designing hierarchical porous TiO2 based anodes for high-performance LIBs.