The Al promotional effect for Ce0.4Zr0.6O2 mixed oxides in selective catalytic oxidation of ammonia to nitrogen
发表时间：2019-03-09
点击次数：
- 论文类型：
- 期刊论文
- 第一作者：
- Wang, Zhong
- 通讯作者：
- Qu, ZP (reprint author), Dalian Univ Technol, Sch Environm Sci & Technol, Key Lab Ind Ecol & Environm Engn MOE, Linggong Rd 2, Dalian 116024, Peoples R China.
- 合写作者：
- Qu, Zhenping,Fan, Rui
- 发表时间：
- 2015-06-16
- 发表刊物：
- SEPARATION AND PURIFICATION TECHNOLOGY
- 收录刊物：
- SCIE、EI、Scopus
- 文献类型：
- J
- 卷号：
- 147
- 页面范围：
- 24-31
- ISSN号：
- 1383-5866
- 关键字：
- NH3 oxidation; Ce0.4Zr0.6O2 catalyst; Al modified; Oxygen species; Oxygen vacancy
- 摘要：
- A novel Al doped Ce0.4Zr0.6O2 catalyst prepared by surfactant-templated method was tested for NH3 selective oxidation, and it was found that the addition of an appropriate amount of Al to Ce0.4Zr0.6O2 catalysts improved the NH3 oxidation activity. Strikingly, the NH3 conversion obtained on 3% Al-Ce0.4Zr0.6O2 catalyst was, on average, 12.7% higher than that of undoped Ce0.4Zr0.6O2 catalyst. The XRD and H-2-TPR results showed that the inclusion of Al components resulted in the formation of smaller sized CeO2 (4.4-5.8 nm), and improved the oxygen mobility and reducibility. The normalized BET and NH3-TPD analysis also confirmed that the adsorption centers for NH3 in Al-Ce0.4Zr0.6O2 catalysts was increased with the Al addition. More importantly, the oxygen vacancies, of which the amount was increased by modification of Al, were considered as the essential oxygen adsorption and activation sites. Consequently, more active oxygen species (O- and O2-) were formed, which facilitated the NH3 oxidation reaction. (C) 2015 Elsevier B.V. All rights reserved.