Investigation of factors influencing the catalytic performance of CO oxidation over Au-Ag/SBA-15 catalyst
发表时间：2019-03-09
点击次数：
- 论文类型：
- 期刊论文
- 第一作者：
- Qu, Zhenping
- 通讯作者：
- Qu, ZP (reprint author), Dalian Univ Technol, Sch Environm Sci & Technol, Key Lab Ind Ecol & Environm Engn MOE, Linggong Rd 2, Dalian 116024, Peoples R China.
- 合写作者：
- Ke, Guozhou,Wang, Yi,Liu, Mengwei,Jiang, Tingting,Gao, Jinsuo
- 发表时间：
- 2013-07-15
- 发表刊物：
- APPLIED SURFACE SCIENCE
- 收录刊物：
- SCIE、EI
- 文献类型：
- J
- 卷号：
- 277
- 页面范围：
- 293-301
- ISSN号：
- 0169-4332
- 关键字：
- Au-Ag; Low metal loading; CO oxidation; SBA-15; Alloy
- 摘要：
- Au-Ag bimetallic nanoparticles (NPs) supported on SBA-15 have been prepared by a two-step method and characterized by ICP-AES, XRD, UV-vis, TG-DTG, XPS and TEM. Au-Ag/SBA-15 bimetallic catalyst with a low metal loading of 1.26 wt.% exhibited high catalytic performance for low temperature CO oxidation, which was governed by Au/Ag molar ratio and the pretreatment conditions (calcination and reduction). The Au-Ag/SBA-15 with an actual Au/Ag molar ratio of 5.4/1 showed the highest catalytic activity for CO oxidation (T-100 = 20 degrees C), and it has also been found that catalytic activity was strongly related with the calcination and reduction temperature of the bimetallic catalyst. The initial CO conversion was increased with the calcination temperature and then decreased above 500 degrees C. It was necessary to activate the bimetallic catalyst and completely remove the amine groups in the catalyst at 500 degrees C for the high activity of CO oxidation. The severe sintering of Au-Ag bimetallic NPs at 700 degrees C resulted in an obvious loss of activity. H-2 reduction following the calcination played an important role in the enhancement of catalytic activity for CO oxidation. The best catalytic performance was obtained in the activation temperature range of 500-600 degrees C, and then decreased with a further increase of reduction temperature to 700 degrees C. The reduction treatment induced the surface redistribution of gold and silver. The formation of a closer bulk value of the surface Au/Ag molar ratio after reduction at 500-600 degrees C and a more random alloy resulted in the improvement in activity. However, the surface enrichment of Ag NPs and the severe aggregation of particles after high temperature reduction (>600 degrees C) caused the activity decrease. (c) 2013 Elsevier B.V. All rights reserved.